Porous
carbon (PC) is obtained by carbonizing a
zinc-coordination
polymer (MOF-5) at 950 °C and PtM (M = Fe, Co, Ni, Cu, Zn) nanoparticles (NPs), which are deposited on PC using the
polyol method. Structural and morphological characterizations of the synthesized materials are carried out by
powder X-ray diffraction (PXRD), X-ray photoelectron spectroscopy (XPS), and high-resolution transmission electron microscopy (HRTEM), and the porosity was determined using a N2 adsorption/desorption technique. The results revealed that PtM NPs are alloyed in the fcc phase and are well dispersed on the surface of PC. The electrochemical results show that PtM/PC 950 catalysts have higher
methanol oxidation reaction (MOR) performances than commercial Pt/C (20%) catalysts. After 3000 s of chronoamperometry (CA) test, the MOR performances decreased in the order of Pt1Cu1/PC 950 > Pt1Ni1/PC 950 > Pt1Fe1/PC 950 > Pt1Zn1/PC 950 > Pt1Co1/PC 950. The high MOR activities of the synthesized catalysts are attributed to the effect of M on
methanol dissociative chemisorption and improved tolerance of Pt against CO
poisoning. The high specific surface area and porosity of the
carbon support have an additional effect in boosting the MOR activities. Screening of the first row transition metals (d 5+n , n = 1, 2, 3, 4, 5) alloyed with Pt binary catalysts for MOR shows that Pt with d 8 (Ni) and d 9 (Cu) transition metals, in equivalent atomic ratios, are good
anode catalysts for alcohol fuel cells.