Morphology and vulcanizate properties of ethylene-propylene-diene rubber/ styrene-butadiene rubber blends.

Abstract

Morphology and vulcanizate properties of EPDM/SBR blends were investigated. AAHR (a mixture of aliphatic and aromatic hydrocarbon resins) was used as a compatibilizer and bis(3-triethoxysilylpropyl)tetrasulfide (TESPT) was used as a coupling agent. The vulcanizate properties and the morphological studies revealed that EPDM and SBR were incompatible, and the addition of AAHR was very effective to enhance the compatibility between EPDM and SBR. The weight percent of bound rubbers was increased with increasing SBR contents. The addition of an AAHR increased the amounts of bound rubbers, and hence the vulcanizate properties such as tear strength and fatigue resistance of the EPDM/SBR blends were improved. The dynamic mechanical analysis and the morphological studies revealed that the addition of TESPT increased the weight of bound rubbers and provided better dispersion of carbon black, resulting in good mechanical properties such as tear strength and fatigue resistance of the vulcanized EPDM/SBR blends. The smaller particle of zinc oxide (i.e., 50 nm > 100 nm > 1000 nm) yielded to the better blending properties of the polymer blend.

• Authors: Gayoung Park, Yun Hee Kim, Dong Soo Kim, Young Chun Ko
• Journal: Journal of nanoscience and nanotechnology (J Nanosci Nanotechnol) Vol. 10 Issue 5 Pg. 3720-2 (May 2010) ISSN: 1533-4880 [Print] United States
• PMID: 20359035 (Publication Type: Journal Article, Research Support, Non-U.S. Gov't)